High-temperature properties of SiC-Si3N4 particle composites
|
| Woetting, G.;Caspers, B.;Gugel, E.;Westerheide, R. 单 位： CFI GmbH Journal of Engineering for Gas Turbines and Power v 122 n 1 January 2000. p 8-12 |
关键词 Silicon carbide;Composite materials;High temperature properties;Sintering;Hot pressing 摘 要Due to promising results in literature, SiC-Si//3N//4 particle composites in the range 0-100 percent SiC were evaluated.Focusing on high-temperature properties, mainly Y//2O//3 was used as sintering additive.Consolidation occured primarily by hot-pressing, sintering tests were performed for comparison.Besides short-term properties like strength, toughness etc., long-term properties like creep and oxidation behavior were determined.Results as a function of SiC-content and microstructure were discussed with respect to materials' performance at high temperatures and possibilities of their production on a technical scale.